產(chǎn)品與市場
Autolad1G
特點
● 適用于無鉛制程，并具有優(yōu)異的耐離子遷移性能
● 在超薄規(guī)格上兼?zhèn)漭^低Z軸CTE及優(yōu)異尺寸穩(wěn)定性
● 不含鹵素、銻、紅磷等成分
應(yīng)用領(lǐng)域
適用于HDI汽車電子，如攝像頭模組等
- 產(chǎn)品性能
- 產(chǎn)品證書
- 資料下載
| Items | Method | Condition | Unit | Typical Value | |
| Tg | IPC-TM-650 2.4.25D | DSC | ℃ | 173 | |
| Td | IPC-TM-650 2.4.24.6 | TGA(5% W.L) | ℃ | 400 | |
| T288 | IPC-TM-650 2.4.24.1 | TMA | min | 60 | |
| CTE (Z-axis) | IPC-TM-650 2.4.24 | Before Tg | ppm/℃ | 35 | |
| After Tg | ppm/℃ | 189 | |||
| 50-260℃ | % | 2.3 | |||
| DK (RC:50%) | 1GHz | IPC-TM-650 2.5.5.9 | C-24/23/50 | -- | 4.30 |
| 10GHz | IPC-TM-650 2.5.5.5 | -- | 4.05 | ||
| Df (RC:50%) | 1GHz | IPC-TM-650 2.5.5.9 | C-24/23/50 | -- | 0.010 |
| 10GHz | IPC-TM-650 2.5.5.5 | -- | 0.012 | ||
| Volume Resistivity | IPC-TM-650 2.5.17.1 | C-96/35/90 | MΩ.cm | 6.00E+08 | |
| Surface Resistivity | IPC-TM-650 2.5.17.1 | C-96/35/90 | MΩ | 8.00E+07 | |
| Dielectric Breakdown | IPC-TM-650 2.5.6 | D-48/50+D-0.5/23 | kV | 45+Kv NB | |
| Peel Strength (1 oz) | IPC-TM-650 2.4.8 | 288℃,10s | N/mm[lb/in] | 1.35 [7.71] | |
| Flexural Strength (LW/CW) | IPC-TM-650 2.4.4 | A | MPa | 550/430 | |
| Flexural Modulus (LW/CW) | IPC-TM-650 2.4.4 | A | GPa | 28/25 | |
| Water Absorption | IPC-TM-650 2.6.2.1 | D-24/23 | % | 0.09 | |
| Flammability | UL94 | C-48/23/50 | Rating | V-0 | |
Remarks:
Remark:
1. All the typical value is based onthe 1.6mm (8*7628) specimen. The Dk and Df value based on 50% RC.
2. All the typical value listed above isfor your reference only, please turn to Shengyi Technology Co., Ltd for detailedinformation, and all rights from this data sheet are reserved by ShengyiTechnology Co., Ltd.
Explanations:C=Humidity conditioning; D=Immersion conditioning in distilled water;E=Temperature conditioning.
The figures following the letter symbolsindicate with the first digit the duration of the preconditioning in hours,with the second digit the preconditioning temperature in ℃ and with the third digit the relative humidity.